Photosensitive resin for SLA/DLP 3D printers

FOB Reference Price:Get Latest Price
US $100-130 / Kilograms | 5 Kilogram/Kilograms (Min. Order)
Report Suspicious Activity
Overview
Quick Details
Place of Origin:
Fujian, China (Mainland)
Classification:
Other Adhesives
Main Raw Material:
Epoxy
Usage:
3D PRINT
Brand Name:
APS
Model Number:
UV-800
Type:
UV Resin
Packaging & Delivery
Packaging Details
1KG/5KG
Port
XIAMEN
Lead Time :
Shipped in 10 days after payment
Product Description

 

INTRODUCTION

UV-800 is one kind of epoxy modified acrylic polymer, it is one component ultraviolet curing resin, low viscosity, no solvent and no volatile. It cured fast under 355nm wave length with smooth surface, also with high strength and excellent toughness properties after cured, it belongs to high performance resin, specialized designed for 3D printing application.   

It is widely used for making: model, first article, first parts, automobile components, medical apparatus and instruments, daily and electronic sample piece, conceptual model, functional components and so on.

MAIN FEATURES

1)One component, fast cure.

2)Low viscosity, easy for operation.

3)Cured with smooth and flat surface.

4)High strength with excellent toughness.

5)High temperature resistance and water-proof.

6)Good stability on product size and high precision. 

7)3D printing any model / article / parts / components you want.

NOTICE AND STORAGE

1)This product belongs to photosensitive adhesive; it should be avoid lights to store.

2)Please store in room temperature (<40 centigrade), cool, dark and dry place.

3)Please ensure the air-tightness, seal the cap well after each use.

4)Please prohibit interfuse the moisture, alcohols and other impurities, these impurities contact might affect the cure effect, in severe case, the resin won’t cure.

 

PROPERTY

Item

Parameter

Uncured

Appearance

White liquid

Viscosity (25, mPa.s)

265.1

Density (25, g/cm3)

1.12

Depth of cure (Dp, mm)

0.16

Critical exposure (EC, mJ/cm2)

6.8

Construct layer thickness (mm)

0.1

Cured              (after 90min)

Appearance

White smooth and flat plastic

Hardness (Shore D)

ASTM D 2240

90

Flexural modulus (MPa)

ASTM D 790

2050-2485

Bending strength (MPa)

ASTM D 790

65-78

Tensile modulus (MPa)

ASTM D 638

1990-2450

Tensile strength (MPa)

ASTM D 638

42-65

Elongation at break (%)

ASTM D 638

14-20

Notched impact strength (J/m)

ASTM D 256

50-65

 

 

                      